1.2083 steel is a martensitic stainless steel with 12% Chromium which is sufficient to give good corrosive resistance properties. It's best corrosive resistance is when hardened and surface is ground or polished. It has good ductility in the annealed condition but can be hardened up to 500HB (highest of the chromium grades). Martensitic Grades are known for high hardness and allowances must be made for poor weldability and usually allowances for a final harden and temper treatment. 420/1.2083 steel is magnetic and welding is not recommended.
Equivalent Grades:
Standard | AISI/SAE | W.Nr/DIN | JIS | GB |
Grade | 420 | 1.2083 | SUJ420J2 | 4Cr13 |
Chemical Composition Of 1.2083 (%)
C | Si | Mn | Mo | P | S | Cr |
0.38-0.45 | ≤1.00 | ≤1.00 | ≤1.00 | ≤0.03 | ≤0.03 | 12.00-13.50 |
Heat Treatment of 1.2083 Steel
Annealing: 760 to 800ºC, slow cooling in furnace (10-20ºC/hr), down to approx. 600ºC, cooling in air. Hardness after annealing: max. 230HB.
Stress relieving: approx. 650ºC, slow cooling in furnace. Hold in neutral atmosphere for 1 to 2hours.
Hardening: 1000 to 1030ºC, oil. Quenching: oil. Hot bath at approx. 300ºC. Hardness obtainable, approx. 56 HRC.
Tempering: Slowly heating to tempering temperature right after hardening. Recommended to temper 2 or 3 times.
Tempering ºC |
100 |
200 |
300 |
400 |
500 |
HRC |
55 |
53 |
52 |
51 |
50 |
* Hardening temperature: 1000ºC, specimen size: dia25mm
Properties:
Well hardening with minimum distortion, very good resistance to wear and compression. In the heat treated condition this steel grade allows a very high polish
Applications:
Inserts and smaller moulds for injection and compression of corrosive plastic materials.
Available Size:
|
||||
Round: | Dia 12-200mm | Hot Rolled | ||
Dia 50-600mm | Forged | |||
Flat/Square: | Thickness | 12-180mm | Hot Rolled | |
20-600mm | Hot Forged | |||
Width | 1000mm Max. |
Q1: What do you do for the control of the quality?
A1: Before loading into the container, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per customer's request.
Q2:: What are your hot-selling products?
A2: D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8, abundant stock for both plates and rounds. Competitive prices and short lead-time.
Q3: Can we visit your company and factory?
A3: Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.
Q4: Are you a manufacturer or merely a trader?
A4: We are a group of companies and owned manufacturer bases and trading companies. We specialized in plastic mold steel, hot work mold steel, cold work mold steel, alloy steel for mechanical, high-speed steel, etc. All materials are of high quality and competitive price.