Die Steel 1.2083 4Cr13 420 Round Bar

• After-sales Service: Online Technical Support
• Warranty: 1 Year
• Standard: ASTM, AISI, GB, JIS, DIN, BS
• Certification: ISO, RoHS
• Surface Treatment: Milling
• Technique: Forged
• Application: Mold & Dies
• Special Use: High-strength Steel Plate, Wear Resistant Steel
• Stock: Stock
• Steel Grade: 1.2083/4Cr13/420
• Surface: Black/Milled/Machined
• Producing Condition: Pre-Harden or Annealed
• Condition: Two Sides or Four Sides Cut for Flat Bar
• Ultrasonic Test Standard: Sep1921-84 E/E with 100% Test
• Shape: Flat Bars/Plates/Blocks/Round Bars
• MOQ: 10 Tons
• Delivery Time: Within 5days
• Mill Sheet Certificate: Provided
• Delivery Type: Shipping
• Steel Remarks: Customized
• Specification: Thickness 5-500mm or Diameter 10-500mm
• Trademark: Chimold
• Origin: China
• HS Code: 722840
• Production Capacity: 10000 Tons Per Month

Product Description

 

Product Description

Die Steel 1.2083 4Cr13 420 Round Bar

 Basic Information

Steel Grade	1.2083/4Cr13/420
Dimension	Thickness 5-500mm  / Diameter 10-500mm
Delivery Condition	Pre-harden or Annealed
Surface Treatment	Black Surface / Milled Surface
Production Condition	Two Sides Cut or Four Sides Cut for Flat Bar
Stock Quantity	2500 tons
Ultrasonic Test	Sep1921-84 D/D or E/e with 100% Test
Lead Time	7-10 days

Product Description

Plastic Mold Steel DIN 1.2083

1.2083 steel is a martensitic stainless steel with 12% Chromium which is sufficient to give good corrosive resistance properties. It's best corrosive resistance is when hardened and surface is ground or polished. It has good ductility in the annealed condition but can be hardened up to 500HB (highest of the chromium grades). Martensitic Grades are known for high hardness and allowances must be made for poor weldability and usually allowances for a final harden and temper treatment.  420/1.2083 steel is magnetic and welding is not recommended.

Equivalent Grades:

Standard	AISI/SAE	W.Nr/DIN	JIS	GB
Grade	420	1.2083	SUJ420J2	4Cr13

 

Chemical Composition Of 1.2083 (%)

C	Si	Mn	Mo	P	S	Cr
0.38-0.45	≤1.00	≤1.00	≤1.00	≤0.03	≤0.03	12.00-13.50

 

Heat Treatment of 1.2083 Steel

Annealing: 760 to 800ºC, slow cooling in furnace (10-20ºC/hr), down to approx. 600ºC, cooling in air. Hardness after annealing: max. 230HB.

Stress relieving: approx. 650ºC, slow cooling in furnace. Hold in neutral atmosphere for 1 to 2hours.

Hardening: 1000 to 1030ºC, oil. Quenching: oil.  Hot bath at approx. 300ºC. Hardness obtainable, approx. 56 HRC.

Tempering: Slowly heating to tempering temperature right after hardening. Recommended to temper 2 or 3 times.

Tempering ºC	100	200	300	400	500
HRC	55	53	52	51	50

* Hardening temperature: 1000ºC, specimen size: dia25mm

Properties:

Well hardening with minimum distortion, very good resistance to wear and compression. In the heat treated condition this steel grade allows a very high polish

Applications:

Inserts and smaller moulds for injection and compression of corrosive plastic materials.

 

Detailed Photos

FAQ

FAQ


Q1: Are you a manufacturer or merely a trader? 
A1: We are not only a stockist of Hot rolled products but also a manufacturer of forged products with our own Forging Mill

Q2: What do you do to control the quality?
A2:  Before loading, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per the customer's request.

Q3:: What are your hot-selling products?
A3: S50C, 1.2311, D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8, abundant stock for both plates and rounds. Competitive prices and short lead-time.

Q4: Can we visit your company and factory? 
A4: Yes, warmly welcome! We will book the hotel and assign our driver to pick you up at the airport when you visit.